Encompassing nanoscale thin twins in metals induces diverse influences, either strengthening triggered by the lattice dislocation blockage effects or softening prompted by dislocation emission from coherent twin boundary (CTB)/grain boundary (GB) intersections as well as CTB migration; yet the deformation mechanism remains poorly understood in ceramic nanostructures possessing covalent bonds.